QLC1104 Conductive Carbon Paste - Conductive Carbon Paste - 联系我们福布斯有限公司开户电话15012099998（福布斯）

Conductive Carbon Paste

QLC1104 Conductive Carbon Paste is a nano-carbon paste designed for flexible printing. It adopts independently developed carbon black particle dispersion technology and paste formulation, featuring excellent printability and adhesion. It can be printed on various substrates such as PI, PCB and paperboard, forming a uniform film and providing a highly reliable solution for flexible printing.

QLC1104 Conductive Carbon PasteAdvantages

Use 150-200 mesh screen for screen printing;

Take the paste out of low-temperature storage and place it at room temperature (25℃) for 1–2 hours. Wipe off any moisture on the container surface before opening. After temperature recovery, stir the paste at 400 r/min for 5–10 minutes to ensure uniform dispersion.;

Recommended printing thickness: 20-30um (i.e., 0.8-1.2 mils);

Ready-to-use Product: No diluent is required before application;

Suitable substrates: PI, paperboard, PCB, etc.;

Recommended cleaneing agent: DBE;

Basic Parameters

Indicators	Performance	Test Condition
Appearance	Black	Visual Inspection
Solid Content	30-60%	/
Viscosity	32000-65000cp	5rpm, 25℃, CPA-512 Rotor
Adhesion	5B	Vertical Pull Test with 3M 600 Adhesive Tape
Curing Conditions	250℃, 30 minutes	/
Storage Life	6 months	Sealed at 0-8℃
Sheet Resistance	50-650 Ω/□	@25um

Product Performance

①Use 150-200 mesh screen for screen printing;

②Take the paste out of low-temperature storage and place it at room temperature (25℃) for 1–2 hours. Wipe off any moisture on the container surface before opening. After temperature recovery, stir the paste at 400 r/min for 5–10 minutes to ensure uniform dispersion.;

③Recommended printing thickness: 20-30um (i.e., 0.8-1.2 mils);

④Ready-to-use Product: No diluent is required before application;

⑤Suitable substrates: PI, paperboard, PCB, etc.;

⑥Recommended cleaneing agent: DBE;